Authors: FangFang Wang Hui Wang Kang Zheng Lin Chen Xian Zhang XingYou Tian
Publish Date: 2013/12/19
Volume: 292, Issue: 4, Pages: 953-963
Abstract
Polybutylene terephthalate PBT/attapulgite AT nanocomposites were prepared by in situ polymerization Morphology of the PBT/AT nanocomposites was observed by scanning electron microscope and polarizing optical microscope Thermogravimetric analyses were used to examine the thermal stability The melting behaviors equilibrium melting temperature isothermal crystallization behavior of pure PBT and PBT/AT nanocomposites were studied by differential scanning calorimetry The results show that PBT/AT nanocomposites possess higher thermal stability than pure PBT and AT nanoparticles play a heterogeneous nucleating agent in PBT crystallization that accelerated the crystallization rate The PBT/AT nanocomposite with higher AT content could retard the transport of polymer chains to the growing crystals compared with that of PBT/AT nanocomposite in lower AT content According to dynamic mechanical analysis results the storage modulus of PBT/AT nanocomposites was markedly improved and the addition of AT nanoparticles promotes the crystallization of PBT which decreases the amorphous area Meanwhile the welldispersed AT nanoparticles also retard the movement of polymer chain segment and increase the proportion of rigid amorphous region
Keywords: