Authors: T Komatsu K Matusita R Yokota
Publish Date: 1985/09/01
Volume: 20, Issue: 9, Pages: 3271-3276
Abstract
Changes in Curie temperature ΔTc electrical resistivity Δϱ/ϱ and volume ΔV/V caused by isochronal annealing in asquenched and preannealed Fe27Ni53P14B6 metallic glasses were compared It was found that the ΔTc against annealing temperature Ta curves in asquenched and preannealed samples are very similar to the Δϱ/ϱ against Ta curves Particularly almost a linear relationship was observed between ΔTc and Δϱ/ϱ in the preannealed sample The results strongly suggest that the origins of both ΔTc and Δϱ/ϱ during structural relaxation in the preannealed sample are attributed to identical reversible shortrange ordering