Authors: S Salimi H Izadi A P Gerlich
Publish Date: 2010/09/02
Volume: 46, Issue: 2, Pages: 409-415
Abstract
Accumulative rollbonding was adapted to fabricate a carbon nanotube CNTreinforced aluminum matrix composite Its microstructure was investigated by transmission electron microscopy and it was confirmed that the nanotubes were embedded into the metal matrix while maintaining their multiwalled structure Measurements revealed that the asreceived CNTs had a bimodal diameter size distribution while only nanotubes with diameters 30 nm and 30 walls were retained during four consecutive rolling operations at 50 reduction